Rail clip, or called elastic rail clip, is used to fasten steel rails to the underlying tie plate. Through bending and distortion, rail clip can put pressure on the rail, which prevents longitudinal movement of the rail, either from changes in temperature or through vibration. In general, rail clips are made of forged spring steel produced by hot forging process. Because of the most uniform microstructure, the forged rail clips are considered to be better than other metal forming process.
Parameters of Main Rail Clip Products
| Model | Diameter | Weight | Material |
| Type III | Ø18 | 0.80kg/pc | 60Si2MnA |
| E1609 | Ø16 | 0.43 kg/pc | 60Si2MnA |
| E1809 | Ø20 | 0.61kg/pc | 60Si2MnA |
| E1813 | Ø18 | 0.62kg/pc | 60Si2MnA |
| E2001 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2007 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2009 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2039 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2055 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2056 | Ø20 | 0.80kg/pc | 60Si2MnA |
| E2063 | Ø20 | 0.80kg/pc | 60Si2MnA |
| PR85 Rail Clip | Ø13 | 0.25kg/pc | 60Si2MnA |
| PR309A | Ø19 | 0.85kg/pc | 60Si2MnA |
| PR401 | Ø20 | 0.97kg/pc | 60Si2MnA |
| PR415 | Ø20 | 0.95kg/pc | 60Si2MnA |
| PR601A | Ø20 | 1.03kg/pc | 38Si7 |
| SKL 1 | Ø13 | 0.48kg/pc | 60Si2CrA |
| SKL 3 | Ø13 | 0.48kg/pc | 60Si2CrA |
| SKL 12 | Ø13 | 0.53kg/pc | 38Si7 |
| SKL 14 | Ø13 | 0.53kg/pc | 60Si2MnA |
| Special Rail Clip | Ø13 | 0.48kg/pc | 60Si2MnA |
| Russia Rail Clip | Ø18 | 0.58kg/pc | 60Si2MnA |
| Deenik Clip | Ø25 | 0.49-0.68kg/pc | 60Si2MnA |
| Single Anti- | Ø20 | 0.25kg/pc | 60Si2MnA |
| Theft |
Factors to Consider before buying Rail Elastic Clips
Before purchasing railway elastic clips, several factors must be considered to ensure long-term, safe, and stable support of the track system. First, material is crucial. Common materials include 60Si2MnA, 60Si2CrA, 55Si2Mn, etc. The elasticity, hardness, and fatigue resistance of these materials directly affect the service life and clamping force of the clip.
| Material | 60Si2MnA | 60Si2CrA | 55Si2Mn | 38Si7 |
| Chemical composition(%) | C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 | C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 | C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 | C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
Second, specifications and size compatibility are critical. The diameter, length, and spring strength of the clip must match the rail type and sleeper, such as P50, P60, QU70, or DIN536 standard rails. Mismatched specifications may result in loose rails or excessive stress, affecting track stability.
Third, environmental adaptability should be evaluated. Coastal, high-temperature, high-humidity, or mining environments require high corrosion and wear resistance. Clips with hot-dip galvanizing, phosphating, or painting treatments are recommended for long-term performance under harsh conditions.
Installation and maintenance requirements are also important. High-quality elastic clips should be easy to install and remove, and compatible with bolts, nuts, fishplates, rail pads, and base plates to form a complete fastening system, ensuring stability under longitudinal and lateral loads.
Supplier service and technical support should also be considered. Choosing a supplier like GNEE RAIL, which offers customization, technical consultation, and installation guidance, allows for adjustments in clip size, material, and surface treatment according to project requirements, optimizing track performance and extending service life.
GNEE RAIL has strict test and completely authentication at every single step of manufacturing rail clips and a full set of quality control system, from raw material purchasing to the finished rail clip packing. We have a professional inspection team to check about each process of the production line.