Pandrol E Clip Specifications
The Pandrol e-Clip rail clip fastening is the preferred fastening system of rail operators across the globe thanks to its versatility and track record for high performance. The ballasted, non-threaded, self-tensioning railway e-Clip system has been installed in over 50 countries across hundreds of applications – covering virtually every possible known rail section.
1. Specification: E1800, E2005, E2007, E2009, E2055 etc.
2. Material: 60Si2Mn
3. Clamping force: 8-12Kn
4. Fatigue life: No less than 5 millions cycles
5. Application: Rail fastening
| Model | Diameter | Material | Under Pressure | HRC | Weight |
| E1609 | Ø 16mm | 60Si2MnA | ≥950kg | 44-48 | 0.43kg/pc |
| E1809 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.61kg/pc |
| E1813 | Ø 18mm | 60Si2MnA | ≥950kg | 44-48 | 0.62kg/pc |
| E2001 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2009 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2039 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2007 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2055 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2056 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
| E2063 | Ø 20mm | 60Si2MnA | ≥950kg | 44-48 | 0.80kg/pc |
Types of E Clip Fasteners
E rail clip provide positive and durable rail alignment under the harshest working conditions, which extend the life of railway track. Generally, e rail clips are available at the range from 18mm to 23mm diameter. Rail –e clip is usually made of spring steel.
| Name | E-type rail clip |
| Material | 60Si2MnA 60Si2CrA 55Si2Mn 38Si7 |
| Hardness | 44-48HRC |
| Fatigue Life | for Dia.18 is 3 millions cycles without breaking |
| for Dia.20 is 5 millions cycles without breaking | |
| Surface | plain (oiled), Oxide black, color painting or according to customer requirement |
| Standard | DIN17221, BS970, GB/T1222 |
Advantages of Using Spring Steel to Manufacture E Type Rail Clips
Spring steel is a resilient, durable steel alloy designed to bend, twist, and compress without permanent distortion, thanks to its high yield strength achieved through heat treatment or work hardening. It's a high-carbon steel rich in elements like manganese, silicon, and chromium, known for returning to its original shape after stress.
| Material | 60Si2MnA | 60Si2CrA | 55Si2Mn | 38Si7 |
| Chemical composition(%) | C:0.56-0.64, Mn:0.60-0.90, Si:1.60-2.00, Cr:≤0.35, P:≤0.03, S:≤0.03 | C:0.56-0.64, Mn:0.40-0.70, Si:1.40-1.80,Cr:0.70-1.00 P:≤0.03, S:≤0.03 | C:0.52-0.60, Mn:0.60-0.90, Si:1.50-2.00,Cr:≤0.35 P:≤0.03, S:≤0.03 | C:0.35-0.42, Mn:0.50-0.80, Si:1.50-1.80, P:≤0.03, S:≤0.03 |
As an OEM & OBM manufacturer, GNEE RAIL is capable of not only producing a wide range of internationally common types of rail clips, such as W Tension Clamp, e-Clip, Fast-Clip, SKL Tension Clamp, Nabla Blade, etc., but also customizing products tailored to our customers' specific requirements.